AM60B 8kg
This alloy reveals an excellent combination of strength, ductility, energy absorption properties and castability. The alloy generally considered for applications which require ductile failure modes such as seat frames, instrumental panels, brackets etc. This product is being produced in the form of 8 kg ingots.
Chemical Composition
Composition in % (Max)
AM60B
Mg
Remainder
Al
5.6-6.4
Mn
0.26-0.50
Zn
0.2
Si
0.05
Cu
0.008
Ni
0.001
Fe
0.004
Other elements each
0.01
Key Benefits
- Produced in accordance with the strictest quality control guidelines
- Lowest CO2 emitting magnesium production process
- Secure raw material source to support global demand
- A geographic location that offers competitive logistic advantages through proximity to ports and customers
8 Kg Ingot Dimensions
Weight
8kg / 17.6lb
Length
627mm / 24.7ln
Width
128mm / 5ln
Height
67mm / 2.6 in
Standard Package
Ingots
124
Layers
13
Weight
1488kg / 3280lb
Length
1254mm / 49.4 inch
Width
627mm / 24.7 inch
Height
1326mm / 52.2 inch
Mechanical Properties
Properties
AM60B
Tensile yield strength [MPa]
20°C
130
150C
90
Ultimate tensile strength [MPa]
20°C
270
150°C
145
Compression yield strength [MPa]
130
Elongation in 50 mm [%]
16
Impact strength [J](2)
19
Young’s Modulus [GPa]
45
Hardness, Brinell
65
Fatigue strength [MPa](3)
90
Creep strength:
Stress to produce 0.2% strain
in 100 hr at 150°C [MPa]
Typical Physical Properties
Properties
AM60B
Density at 20°C [g/cm3 ]
1.80
Lin.thermal exp.
Coeff [μm/m.K] at
26.0
20-100•c
Thermal conductivity
61
[W/K m] at 20’C
Electrical conductivity
7.9
at 20’C[W/K.m)
Specific heat [kJ/kg K]
1.02
at 20’C
latent heat of fusion
370
[kJ/kg]
Non-equilibrium
615-434
Solidification range[°c]